Analisa Pengaruh Letak Susunan Serat Ampas Tebu (Baggase) Terhadap Kekuatan Tarik Menggunakan Epoxy

Prihatno, Asep (2020) Analisa Pengaruh Letak Susunan Serat Ampas Tebu (Baggase) Terhadap Kekuatan Tarik Menggunakan Epoxy. Undergraduate thesis, Politeknik Negeri Bengkalis.

[img]
Preview
Text (Abstrak)
10.SKRIPSI-2204161068-ABSTRAK.pdf - Submitted Version
Available under License Creative Commons Attribution Share Alike.

Download (26kB) | Preview
[img]
Preview
Text (Bab I Pendahuluan)
2.SKRIPSI-2204161068-BAB I.pdf - Submitted Version
Available under License Creative Commons Attribution Share Alike.

Download (21kB) | Preview
[img]
Preview
Text (Daftar Pustaka)
7.SKRIPSI-2204161068-DAFTAR PUSTAKA.pdf - Submitted Version
Available under License Creative Commons Attribution Share Alike.

Download (19kB) | Preview
[img] Text (Full Text)
9.SKRIPSI-2204161068-FULL TEXT.pdf - Submitted Version
Restricted to Registered users only
Available under License Creative Commons Attribution Share Alike.

Download (2MB) | Request a copy

Abstract

Bagasse fiber (baggase) is an organic waste that is widely available in various regions in Indonesia. This research was conducted to determine the strenght of sugarcane bagasse as a substitute composite in which this study conducted variations in the variation of the composition of the fiber woven, cross, and random by comparison volume ratio of epoxy 92 %, 88 %, 84 % with natural fibers 8 %, 12 %, 16 % by performing tensile test testing with ASTMD 638-14 standard by using the hand lay up method composite printing. The results of the tensile test of bagasse fiber for 8% weight of the highest were cross and random fibers of 15.16 MPa, for 12% of weight the highest were cross and random fibers which had a value of 18.71 Mpa, for 16% fibers which had The highest tensile strength values were woven and cross fibers which had a value of 21.69 MPa. This study shows that the addition of sugar cane fiber affects the tensile strength.

Item Type: Thesis (Undergraduate)
Contributors:
ContributionContributorsEmailNIDN/NIDK
Thesis advisorHaripriadi, Bambang Dwibambang@polbeng.ac.idNIDN1030017802
Uncontrolled Keywords: Tensile Strenght, ASTMD 638-14, Fiber Structure, Epoxy Volume
Subjects: 410 ILMU TEKNIK > 430 ILMU KETEKNIKAN INDUSTRI > 431 Teknik Mesin (dan Ilmu Permesinan Lain)
Divisions: Jurusan Teknik Mesin > Sarjana Terapan Teknik Mesin Produksi dan Perawatan > TUGAS AKHIR
Depositing User: Editor Perpustakaan
Date Deposited: 08 Jun 2021 13:48
Last Modified: 08 Jun 2021 13:48
URI: http://eprints.polbeng.ac.id/id/eprint/289

Actions (login required)

View Item View Item