Analisa Komposit Diperkuat Serbuk Serabut Kelapa Bermatrik Epoxy Terhadap Kekuatan Tarik

Ferdianto, Fery (2020) Analisa Komposit Diperkuat Serbuk Serabut Kelapa Bermatrik Epoxy Terhadap Kekuatan Tarik. Undergraduate thesis, Politeknik Negeri Bengkalis.

[img]
Preview
Text (Abstrak)
10. SKRIPSI-2204161081-ABSTRACT.pdf - Submitted Version
Available under License Creative Commons Attribution Share Alike.

Download (103kB) | Preview
[img]
Preview
Text (Bab I Pendahuluan)
2. SKRIPSI-2204161081-BAB I.pdf - Submitted Version
Available under License Creative Commons Attribution Share Alike.

Download (102kB) | Preview
[img]
Preview
Text (Daftar Pustaka)
7. SKRIPSI-2204161081-DAFTAR PUSTAKA.pdf - Submitted Version
Available under License Creative Commons Attribution Share Alike.

Download (74kB) | Preview
[img] Text (Full Text)
9. SKRIPSI-2204161081-FULL TEXT.pdf - Submitted Version
Restricted to Registered users only
Available under License Creative Commons Attribution Share Alike.

Download (4MB) | Request a copy

Abstract

The research conducted aims to determine the value and mechanical properties of the tensile test and determine the fracture characteristics of the specimen. The green coconut powder thet is carried out must be separated from the fiber and the mash size is 2.36 mm, making composites using word molds with a width: 14 cm,length:28.5 cm, thickness: 5 mm. The specimens of the specimens refer to the ASTM D638-14 standar for tensile tests. From the test results, with variations in material content 34% Coconut Fiber Powder + 66% Epoxy Resin, 41% Coconut Fiber Powder + 59% Epoxy Resin, 47 % Coconut Fiber Powder + 53% Epoxy Resin, 52% Coconut Fiber Powder + 48% Epoxy Resin, 58% Coconut Fiber Powder + 42% Epoxy Resin. In the study, the highest maximal tensile strength of the composite with a variation of 41% coconut powder + 59% epoxy resin was over 8.09 N/mm2 and the lowest strength variation was 42% resin and 58% powder with a tensile strength of 4.55 N/mm2 The morphology that blends perfectly well between epoxy resin and coconut powder with a variety of specimens of 59% epoxy resin and 41% coconut fiber powder.

Item Type: Thesis (Undergraduate)
Contributors:
ContributionContributorsEmailNIDN/NIDK
Thesis advisorSuhardiman, Suhardimansuhardiman@polbeng.ac.idUNSPECIFIED
Uncontrolled Keywords: epoxy composite, coconut fiber, test tensile
Subjects: 410 ILMU TEKNIK > 430 ILMU KETEKNIKAN INDUSTRI > 431 Teknik Mesin (dan Ilmu Permesinan Lain)
Divisions: Jurusan Teknik Mesin > Sarjana Terapan Teknik Mesin Produksi dan Perawatan > TUGAS AKHIR
Depositing User: Editor Perpustakaan
Date Deposited: 17 Jun 2021 09:41
Last Modified: 17 Jun 2021 09:43
URI: http://eprints.polbeng.ac.id/id/eprint/345

Actions (login required)

View Item View Item