Pengaruh Penggunaan Bahan Tambah Serat Fiber pada Beton Mutu 25 MPa

Suprianto, Suprianto (2025) Pengaruh Penggunaan Bahan Tambah Serat Fiber pada Beton Mutu 25 MPa. Diploma thesis, Politeknik Negeri Bengkalis.

[thumbnail of Abstract] Text (Abstract)
1.TA-4103221491-Abstract.pdf - Submitted Version
Available under License Creative Commons Attribution Share Alike.

Download (9MB)
[thumbnail of Bab l Pendahuluan] Text (Bab l Pendahuluan)
2.TA-4103221491-Bab l Pendahuluan.pdf - Submitted Version
Available under License Creative Commons Attribution Share Alike.

Download (9MB)
[thumbnail of Daftar Pustaka] Text (Daftar Pustaka)
3.TA-4103221491-Daftar Pustaka.pdf - Submitted Version
Available under License Creative Commons Attribution Share Alike.

Download (9MB)
[thumbnail of Full Text] Text (Full Text)
4.TA-4103221491-Full Text.pdf - Submitted Version
Restricted to Registered users only
Available under License Creative Commons Attribution Share Alike.

Download (9MB)

Abstract

Concrete technology has developed in various ways, both through the addition of supplementary materials and by partially replacing its constituent components. This study aims to apply and identify the effect of adding fiberglass fibers on the compressive strength, splitting tensile strength,and slump value of concrete with a target strength of fc’ 25 MPa. Tests were conducted on normal concrete and concrete with the addition of fiberglass fibers in variations of 0.3%, 0.5%, and 0.9% by the weight of cement. Concrete specimens in the form of cylinders measuring 10 cm x 20 cm were tested at 28 days of age. Concrete itself consists of coarse aggregate, fine aggregate, cement, and
water as a binder.The results showed that adding fiberglass fibers tended to reduce the compressive strength compared to normal concrete, which had a compressive strength of 20.08 MPa, becoming 14.52 MPa (0.3% variation), 18.54 MPa (0.5% variation), and 17.91 MPa (0.9% variation).However, the addition of fiberglass fibers increased the splitting tensile strength from 2.34 MPa(normal) to 2.44 MPa (0.3%), 3.11 MPa (0.5%), and 3.03 MPa (0.9%). In addition, the slump value also increased from 70 mm (normal concrete) to 80 mm (0.3%) and 90 mm for variations of 0.5% and 0.9%, indicating an improvement in the workability of the concrete mix.

Item Type: Thesis (Diploma)
Uncontrolled Keywords: Splitting Tensile Strength, Compressive Strength, Fiberglass,Slump.
Subjects: 600 – ILMU TEKNIK DAN ILMU TERAPAN > 624 – Teknik Sipil dan Konstruksi > 624.1 – Perencanaan dan Desain Bangunan
600 – ILMU TEKNIK DAN ILMU TERAPAN > 624 – Teknik Sipil dan Konstruksi > 624.2 – Struktur Bangunan dan Material
Divisions: Jurusan Teknik Sipil > Diploma Tiga (D-III) Teknik Sipil > TUGAS AKHIR
Depositing User: D-III Teknik Sipil B 2022
Date Deposited: 01 Sep 2025 03:33
Last Modified: 01 Sep 2025 03:33
URI: https://eprints.polbeng.ac.id/id/eprint/2901

Actions (login required)

View Item
View Item